High Quality Extension Polyolefin Fabric Heat Shrink Tubing in China

Certification: Iatf 16949
Color: Black
IP Rating: V0
Material: PE
Type: Heat Shrinkable
Transport Package: Carton
Samples:
US$ 20/Piece 1 Piece(Min.Order)
| Request Sample
Customization:

Contact Supplier

Diamond Member Since 2018

Suppliers with verified business licenses

Manufacturer/Factory & Trading Company

Basic Info.

Model NO.
CL-KSD
Specification
6-100mm
Origin
Changzhou
Production Capacity
300000m/Month

Product Description

Material(s) Description
Warp material: Polyester
Weft material: Irradiated, modified polyolefin
Coating: Modified polyolefin
Operating temperature range (3000 hours): -40°C to 125°C
Operating temperature range (1000 hours): -40°C to 150°C
Minimum recovery temperature: 110°C
Recommended recovery temperature :150°C to 200°C
Maximum storage temperature: 50°C 
Standard:TL52668    TL52361    D44 1959   GMW14327
Testing organization:CTI  PONY

Product description   (CL-KSD) Inside diameter (mm)
 D (min.) expanded as supplied  d (max.) recovered after heating
φ6/3-B 6 3
φ8/4-B 8 4
φ10/5-B 10 5
φ12/6-B 12 6
φ16/8-B 16 8
φ20/10-B 20 10
φ25/12-B 25 12
φ30/15-B 30 15
φ35/17.5-B 35 17.5
φ40/20-B 40 20
φ50/25-B 50 25
φ60/30-B 60 30
φ70/35-B 70 35
φ80/40-B 80 40
φ100/50-B 100 50
B:black
Other specifications can be customized

 

Property Test condition(s) Performance
Thermal ageing 168 hrs at 125°C No deterioration in abrasion resistance at 23°C
24 hrs at 125°C No deterioration in abrasion resistance at 23°C
Flammability MVSS 302 Burning rate≤100 mm/min
Low temperature flexibility  4 hours at -40°C,10X  diameter mandrel No cracking
Abrasion resistance
(1.5N load, 0.3mm radius metal blade,60 cpm,50mm stroke, 144 000 cycles)

 
Environmental Chamber Temperature: -35°C  No wear to underlying rubber hose
Environmental Chamber Temperature: 140ºC
Temperature resistance
1) Test temperature 140 ºC, for 500 hours
2) Remove the sample and cool it to room temperature..Then place the sample at -35°C for 22 hours.
3) Then bend the sample 180 degrees around a cylinder with a radius of 30mm
Test temperature 140 ºC, for 500 hours
 
The protection tube is not damaged
Standard: TL52668

High Quality Extension Polyolefin Fabric Heat Shrink Tubing in China

High Quality Extension Polyolefin Fabric Heat Shrink Tubing in China
High Quality Extension Polyolefin Fabric Heat Shrink Tubing in China
High Quality Extension Polyolefin Fabric Heat Shrink Tubing in China
High Quality Extension Polyolefin Fabric Heat Shrink Tubing in China
 

Send your message to this supplier

*From:
*To:
avatar Miss Yvonne
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

You Might Also Like

Contact Supplier

Diamond Member Since 2018

Suppliers with verified business licenses

Manufacturer/Factory & Trading Company
Number of Employees
52
Terms of Payment
LC, T/T