Harness Protection Fabric Heat Shrinkable Tubing

• Customization: Available
• Certification: RoHS
• Color: Black
• Model NO.: CL-KSD
• Usage: Abrasion Resistance Automative Hose Protection
• Material: PE+Pet
• Type: Heat Shrinkable
• Transport Package: Carton
• Specification: Customizable
• Origin: Changzhou
• Production Capacity: 12000000m/Year

Product Description

Material(s) Description

• Warp material              Polyester
• Weft material               Irradiated, modified polyolefin
• Coating                        Modified polyolefin

The material is composed of polyester fiber material plus high-density polyethylene additive additive and protective coating latex.

The specific composition is as follows:
Standard sizes 

                     Inside diameter (mm)

Product description    D (min.) expanded        d (max.) recovered 
as supplied                 after heating

12/6-B                                  12                                           6

20/10-B                                20                                          10

30/15-B                                30                                          15

40/20-B                                40                                           20

50/25-B                                50                                           25

60/30-B                                60                                           30

70/35-B                                70                                           35

Non-standard high volume sizes

                     Inside diameter (mm)

Product description    D (min.) expanded        d (max.) recovered 
as supplied                 after heating

6/3-B                                     6                                            3

16/8-B                                 16                                            8

25/12-B                               25                                           12

35/17.5-B                            35                                         17.5

80/40-B                               80                                           40

Note: B = Black
Our company can provide the specifications above.

Temperature rating

• Operating temperature range (3000 hours): -40°C to 125°C
• Operating temperature range (1000 hours): -40°C to 150°C
• Minimum recovery temperature: 110°C
• Recommended recovery temperature 150°C to 200°C)
• Maximum storage temperature: 50°C 

Typical KSD Performance

Property	Test condition(s)	Performance
Thermal ageing	168 hrs at 125°C	No deterioration in abrasion resistance at 23°C
	24 hrs at 125°C	No deterioration in abrasion resistance at 23°C
Flammability	MVSS 302	Burning rate≤100 mm/min
Low temperature flexibility	4 hours at -40°C,10X  diameter mandrel	No cracking
Fluid resistance Antifreeze (50% ethylene glycol) Engine oil (SAE 10w/30) Mineral hydraulic fluid Detergent (1% Teepol) Brake fluid (DOT 4) Unleaded gasoline Diesel fuel Battery acid (1.25 SG H2SO4)	24  hours immersion at 23°C	No deterioration in abrasion resistance at 23°C
Abrasion resistance (1.5N load, 0.3mm radius metal blade,60 cpm,50mm stroke, 144 000 cycles)	Environmental Chamber Temperature: -35°C	No wear to underlying rubber hose
	Environmental Chamber Temperature: 140ºC
Pulse test 1) Pressure: 2.5 bar (absolute pressure) 2) Test cycle: 2S 3) Pulse number: 50000	Temperature: 140±5 ºC	The sample protection hose is not torn or worn, and there are no abnormalities such as shedding or leakage at both ends. Standard: TL52668
Temperature resistance 1) Test temperature 140 ºC, for 500 hours 2) Remove the sample and cool it to room temperature..Then place the sample at -35°C for 22 hours. 3) Then bend the sample 180 degrees around a cylinder with a radius of 30mm	Test temperature 140 ºC, for 500 hours	The protection tube is not damaged Standard: TL52668