Heat Shrinkable Sleeve/Tubing

• Certification: RoHS, Iatf 16949
• Color: Black
• Usage: Wire Protection;Hose Protection Sleeve
• Material: PE+Pet
• Type: Heat Shrinkable
• Transport Package: Carton
• Model NO.: CL-KSD
• Specification: Customizable
• Origin: Changzhou
• Production Capacity: 12000000m/Year

Product Description

Material(s) Description
Warp material: Polyester
Weft material: Irradiated, modified polyolefin
Coating: Modified polyolefin
Operating temperature range (3000 hours): -40°C to 125°C
Operating temperature range (1000 hours): -40°C to 150°C
Minimum recovery temperature: 110°C
Recommended recovery temperature: 150°C to 200°C
Maximum storage temperature: 50°C
Standard: TL52668 TL52361 D44 1959 GMW14327
Testing organization: CTI PONY

Product description (CL-KSD)	Inside diameter (mm)
	D (min. ) expanded as supplied	D (max. ) recovered after heating
Φ6/3-B	6	3
Φ8/4-B	8	4
Φ10/5-B	10	5
Φ12/6-B	12	6
Φ16/8-B	16	8
Φ20/10-B	20	10
Φ25/12-B	25	12
Φ30/15-B	30	15
Φ35/17.5-B	35	17.5
Φ40/20-B	40	20
Φ50/25-B	50	25
Φ60/30-B	60	30
Φ70/35-B	70	35
Φ80/40-B	80	40
Φ100/50-B	100	50
B: Black
Other specifications can be customized

Property	Test condition(s)	Performance
Thermal ageing	168 hrs at 125°C	No deterioration in abrasion resistance at 23°C
	24 hrs at 125°C	No deterioration in abrasion resistance at 23°C
Flammability	MVSS 302	Burning rate≤100 mm/min
Low temperature flexibility	4 hours at -40°C, 10X diameter mandrel	No cracking
Abrasion resistance (1.5N load, 0.3mm radius metal blade, 60 cpm, 50mm stroke, 144 000 cycles)	Environmental Chamber Temperature: -35°C	No wear to underlying rubber hose
	Environmental Chamber Temperature: 140ºC
Temperature resistance 1) Test temperature 140 ºC, for 500 hours 2) Remove the sample and cool it to room temperature...Then place the sample at -35°C for 22 hours.  3) Then bend the sample 180 degrees around a cylinder with a radius of 30mm	Test temperature 140 ºC, for 500 hours	The protection tube is not damaged Standard: TL52668